UNS K93600

We can produce UNS K93600 stainless steel round rods, UNS K93600 forging,sheet,coil,and profiledstrip,Deformed steel,flat steel,mould,steel wire,have all specifications. With DuoNian production experience, strict control UNS K93600 chemical composition and UNS K93600 mechanical properties.From casting, forging, steel to hot and cold rolling process, heat treatment, etc, we have the control of professional engineers. We have advanced precision machining equipment, according to the requirements of users machining. in order to achieve the most satisfied with the user requirements.

Production specification

Round bar steel: 1mm to 3500mm
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.

 

Chemical composition % of the ladle analysis of grade 1.3912 and Standards

Material number 1.3912 -

Invar 36
 
 
UNS K93600
W.Nr.1.3912
X1NiCrMoCu
Fe-Ni36

UNS K93600 Composition in % :

 

C

Si

Mn

P

S

Cr

Mo

Ni

max. 0,10

max. 0,50

max. 0,50

max. 0,025

max. 0,025

max. 0,50

max. 0,50

35,0 - 37,0

V

W

Ti

Cu

Al

Nb

Co

Fe

 

 

 

 

 

 

max. 1,00

60,00 - 65,00

 

 

 


UNS K93600Machining performance

 

Download 1.3912 the mechanical properties of the report, the report provides detailed performance analysis and application.


UNS K93600Principal Design Features

 

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


UNS K93600Machinability

 

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


UNS K93600Heat Treatment

 

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


UNS K93600Welding

 

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


UNS K93600Forging

 

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.