DIN X50NiCrWV13-13

We can produce DIN X50NiCrWV13-13 stainless steel round rods, DIN X50NiCrWV13-13 forging,sheet,coil,and profiledstrip,Deformed steel,flat steel,mould,steel wire,have all specifications. With DuoNian production experience, strict control DIN X50NiCrWV13-13 chemical composition and DIN X50NiCrWV13-13 mechanical properties.From casting, forging, steel to hot and cold rolling process, heat treatment, etc, we have the control of professional engineers. We have advanced precision machining equipment, according to the requirements of users machining. in order to achieve the most satisfied with the user requirements.

Production specification

Round bar steel: 1mm to 3500mm
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.

 

DIN X50NiCrWV13-13

LonghaiSteel supply domestic and overseas customers with DIN X50NiCrWV13-13 steel plate, DIN X50NiCrWV13-13 flat steel,DIN X50NiCrWV13-13 steel sheet,DIN X50NiCrWV13-13 wire coil,DIN X50NiCrWV13-13 square bar,DIN X50NiCrWV13-13 round rod, DIN X50NiCrWV13-13 steel pipe,DIN X50NiCrWV13-13forged valve body,DIN X50NiCrWV13-13 forged steel rings,DIN X50NiCrWV13-13 forged multidiameter shafts. Through many years' production experiences,we strictly control DIN X50NiCrWV13-13 chemical composition and mechanical properties from casting, forging, rolling, heat treatment, etc. We have advanced precision machining equipments with a higher productioncapacity,bringinga best service and affordable prices to customersfrom all over the world.

LonghaiSteel are Manufacturers and Suppliers of DIN X50NiCrWV13-13 valve steel with high quality and affordable quotation, If you are keen interested in the valve steel, please feel free to contact with us for more detailed data concerning the valve steel Today! We will serve you with our honesty, integrity, and professionality. And specific features are as follows:

Steel grade & Chemical composition (mass fraction)(%)- Valve Steel
 

Steel grade:  DIN X50NiCrWV13-13

 
C(%):    0.45~0.55
Si(%):    1.20~1.50
Mn(%):    0.60~0.80
P(%)≤:    0.035
S(%)≤:    0.035
Cr(%):    12.0~14.0
Ni(%):    12.50~13.50
Mo(%):    —
Other(%):    W 1.50~2.80,V 0.30~1.00
 

Mechanical property & thermal treatment - Valve Steel
 
 
Hot forming temperature /℃: 1050~850
Heat treatment temperature and cooling method | annealing:    -     
Heat treatment temperature and cooling method | quenching:  1000~1050 oil/water      
Heat treatment temperature and cooling method | tempering:   700~750          
Room temperature mechanical property |σb/MPa:    780~980
Room temperature mechanical property |σs≥/MPa:    390       
Room temperature mechanical property |δ5≥(%):    25        
Room temperature mechanical property |ψ≥(%):    35      
 
Mechanical property above 400℃ σb/MPa,at following temperature /℃|400:    -
Mechanical property above 400℃ σb/MPa,at following temperature /℃|500:    660
Mechanical property above 400℃ σb/MPa,at following temperature /℃|600:    560
Mechanical property above 400℃ σb/MPa,at following temperature /℃|700:    410
Mechanical property above 400℃ σb/MPa,at following temperature /℃|800:    260
 
 

 Main features and Application field:
 
Valve steel is a subbranch of heat resistant steels, the special material is for processing the vent valve & intake valve of combustion engines. This steel material is always under the high temperature 450 ~ 900℃ and in the operating conditions of 3000~7000kPa explosion pressure. It longly stands up to the gas-fired high temperature corrosion,scouring of gasoline,diesel and also friction from valve seats. Hence, the valve steel material must have enough heat resistance,high temperature resistance corrosivity,inoxidizability,abrasive resistance and impact resistance under the highest working temperature.
 

Advantage:

LonghaiSteel have advanced production equipment and a team of professional design team, strict implementation of ISO9001 quality management system
Specialized in high quality steel and best service
forged/hot rolling/ extrusion of steel

Related hot word search:DIN X50NiCrWV13-13 round bar DIN X50NiCrWV13-13,forging DIN X50NiCrWV13-13,DIN X50NiCrWV13-13 sheet,coil DIN X50NiCrWV13-13,DIN X50NiCrWV13-13 flat bar,pipe DIN X50NiCrWV13-13,DIN X50NiCrWV13-13 Lrregular

Prev:W-Nr 1.2731
Next:1.4954