Ti-6Al-4V Ti Alloy

We can produce Ti-6Al-4V Ti Alloy stainless steel round rods, Ti-6Al-4V Ti Alloy forging,sheet,coil,and profiledstrip,Deformed steel,flat steel,mould,steel wire,have all specifications. With DuoNian production experience, strict control Ti-6Al-4V Ti Alloy chemical composition and Ti-6Al-4V Ti Alloy mechanical properties.From casting, forging, steel to hot and cold rolling process, heat treatment, etc, we have the control of professional engineers. We have advanced precision machining equipment, according to the requirements of users machining. in order to achieve the most satisfied with the user requirements.

Production specification

Round bar steel: 1mm to 3500mm
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.

 

Ti-6Al-4V Ti Alloy
Our advantages

Ti-6Al-4V properties and heat treatment forged piece, Including Ti-6Al-4V application and specifications, We have all specifications,Including Ti-6Al-4V steel plate, Ti-6Al-4V sheet, Ti-6Al-4V square steel, Ti-6Al-4V flat bar,Ti-6Al-4V round bar,Ti-6Al-4V forgings, we can own production and sales.


--------------------------------------------------------------------------------
Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


--------------------------------------------------------------------------------

We can produce the Ti-6Al-4V has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


--------------------------------------------------------------------------------
Chemical composition % of the ladle analysis of grade Ti-6Al-4V and Standards

 

Category Titanium Alloy
Class Wrought
Type Alpha-beta alloy
Designations United States: ASTM B265 Grade5, ASTM B348 Grade5, ASTM B381 Grade5, MIL-T-9046, MIL-T-9047, AMS 4928, AMS 4911, AMS 4906, AMS 4965

Composition
Element Weight %
Al  6 
V  4 
 

 

Mechanical Properties
Properties  Conditions
T (°C) Treatment
Density (×1000 kg/m3) 4.43 25  
Poisson's Ratio 0.342 25  
Elastic Modulus (GPa) 113.8 25  
Tensile Strength (Mpa) 993 25 annealed  more
Yield Strength (Mpa) 924
Elongation (%) 14 
Reduction in Area (%) 30 
Hardness (HRC) 36  25 annealed more
Impact Strength (J)
(Charpy) 19 25 annealed  

 

Thermal Properties
Properties  Conditions
T (°C) Treatment
Thermal Expansion (10-6/ºC) 8.6 20-100 more  

 


--------------------------------------------------------------------------------

Machining performance

Download Ti-6Al-4V the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


--------------------------------------------------------------------------------

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


--------------------------------------------------------------------------------

Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


--------------------------------------------------------------------------------

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


--------------------------------------------------------------------------------

Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


--------------------------------------------------------------------------------

Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.


--------------------------------------------------------------------------------

 

Hot tags:Ti-6Al-4V steel plate, Ti-6Al-4V sheet, Ti-6Al-4V square steel, Ti-6Al-4V flat bar,Ti-6Al-4V round bar,Ti-6Al-4V forgings

 

Copyright © 1996-2011 Longhai Special Steel. All Rights Reserved.
Longhai steel is China's special steel inventory spot suppliers.  

The sender: ChenXueYang mobile: 13108107311; Machine: 0816-3653779, 0816-3646884; Fax: 0816-3639422; QQ: 2286637323, E-mail: chinasteelsuppliers. Com
Stainless Steel | Mould steel | Heat resistant steel | Tool steel | Bearing steel | Spring steel | Alloy steel | Nickel base alloy and high nickel containing steels | Cementation steels | Free-cutting steels | Cold extrusion steels | Nitriding steels | Chain steels | Carbon steel | Ti Alloy | High temperature high strength alloy and high-temperature alloy | Low alloy high-temperature steel |

 

Related hot word search:Ti-6Al-4V Ti round bar Ti-6Al-4V Ti Alloy,forging Ti-6Al-4V Ti Alloy,Ti-6Al-4V Ti Alloy sheet,coil Ti-6Al-4V Ti Alloy,Ti-6Al-4V Ti Alloy flat bar,pipe Ti-6Al-4V Ti Alloy,Ti-6Al-4V Ti Alloy Lrregular

Prev:Ti-6Al-4V-ELI (low O2) Ti Alloy
Next:Ti-6Al-2Sn-l.5Zr-1Mo-0.35Bi-0.1Si Ti Alloy