UNS R54520 Ti Alloy

We can produce UNS R54520 Ti Alloy stainless steel round rods, UNS R54520 Ti Alloy forging,sheet,coil,and profiledstrip,Deformed steel,flat steel,mould,steel wire,have all specifications. With DuoNian production experience, strict control UNS R54520 Ti Alloy chemical composition and UNS R54520 Ti Alloy mechanical properties.From casting, forging, steel to hot and cold rolling process, heat treatment, etc, we have the control of professional engineers. We have advanced precision machining equipment, according to the requirements of users machining. in order to achieve the most satisfied with the user requirements.

Production specification

Round bar steel: 1mm to 3500mm
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.

 

Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyUNS R54520 plate,UNS R54520 Round Bar,UNS R54520 forgings,UNS R54520 suppliers, UNS R54520 Stock,UNS R54520 sheet, UNS R54520 flat bar, UNS R54520 pipe,UNS R54520 tube,UNS R54520 mould,UNS R54520 round ingot,UNS R54520 cold-rolled steel,UNS R54520 coil,UNS R54520 strap steel,UNS R54520 hot-rolled steel,UNS R54520 medium plate, UNS R54520 heavy plate,UNS R54520 shapped bar,UNS R54520 hexahedral bar,UNS R54520,UNS R54520 slab ingot,UNS R54520 slab,UNS R54520 price,UNS R54520 square bar,UNS R54520 square steel,UNS R54520 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of UNS R54520.
 
 
UNS R54520 Ti Alloy
Our advantages

UNS R54520 properties and heat treatment forged piece, Including UNS R54520 application and specifications, We have all specifications,Including UNS R54520 steel plate, UNS R54520 sheet, UNS R54520 square steel, UNS R54520 flat bar,UNS R54520 round bar,UNS R54520 forgings, we can own production and sales.


--------------------------------------------------------------------------------

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


--------------------------------------------------------------------------------

We can produce the UNS R54520 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


--------------------------------------------------------------------------------
Chemical composition % of the ladle analysis of grade UNS R54520 and Standards

 

Titanium Ti-5Al-2.5Sn (Grade 6)
Categories:  Metal; Nonferrous Metal; Titanium Alloy; Alpha/Near Alpha Titanium Alloy
Material Notes:  1 other heat treatment of this alloy is in MatWeb.
Key Words:  UNS R54520; Ti-5-2.5

 

 

Physical Properties Metric English Comments
Density 4.48 g/cc 0.162 lb/in³
 
Mechanical Properties Metric English Comments
Hardness, Brinell 320 320
Hardness, Knoop 363 363 Estimated from Rockwell C.
Hardness, Rockwell C 36 36
Hardness, Vickers 349 349 Estimated from Rockwell C.
Tensile Strength, Ultimate 861 MPa 125000 psi
Tensile Strength, Yield 827 MPa 120000 psi
Elongation at Break 15.0 % 15.0 %
Modulus of Elasticity 110 - 125 GPa 16000 - 18100 ksi
Compressive Yield Strength 830 MPa 120000 psi
Notched Tensile Strength 1240 MPa 180000 psi Kt (stress concentration factor) = 6.5
Ultimate Bearing Strength 1760 MPa 255000 psi e/D = 2
Bearing Yield Strength 1340 MPa 194000 psi e/D = 2
Poissons Ratio 0.310 0.310 Typical for alpha titanium alloy.
Charpy Impact 24.0 J 17.7 ft-lb V-notch
Fatigue Strength 290 MPa
@# of Cycles 1.00e+7 42100 psi
@# of Cycles 1.00e+7 Kt (stress concentration factor) = 2.4
  380 MPa
@# of Cycles 1.00e+7 55100 psi
@# of Cycles 1.00e+7 unnotched
  390 MPa
@# of Cycles 100000 56600 psi
@# of Cycles 100000 Kt (stress concentration factor) = 2.4
  440 MPa
@# of Cycles 1.00e+6 63800 psi
@# of Cycles 1.00e+6 unnotched
  530 MPa
@# of Cycles 100000 76900 psi
@# of Cycles 100000 Unnotched
Fracture Toughness 33.0 MPa-m½ 30.0 ksi-in½ K(ISCC)
  96.0 MPa-m½ 87.4 ksi-in½ K(IC)
Shear Modulus 48.0 GPa 6960 ksi
Shear Strength 520 MPa 75400 psi Ultimate shear strength
 
Electrical Properties Metric English Comments
Electrical Resistivity 0.000160 ohm-cm 0.000160 ohm-cm
 
Thermal Properties Metric English Comments
CTE, linear 9.40 µm/m-°C
@Temperature 0.000 - 100 °C 5.22 µin/in-°F
@Temperature 32.0 - 212 °F
  9.50 µm/m-°C
@Temperature 0.000 - 315 °C 5.28 µin/in-°F
@Temperature 32.0 - 599 °F average; unspecified heat treatment.
  9.70 µm/m-°C
@Temperature 0.000 - 650 °C 5.39 µin/in-°F
@Temperature 32.0 - 1200 °F average
Specific Heat Capacity 0.530 J/g-°C 0.127 BTU/lb-°F 0.674 J/g-ºC at 315ºC
Thermal Conductivity 7.80 W/m-K 54.1 BTU-in/hr-ft²-°F 10.9 W/m-ºC at 315ºC
Melting Point <= 1590 °C <= 2890 °F Liquidus
Liquidus 1590 °C 2890 °F
Beta Transus 1040 - 1090 °C 1900 - 1990 °F
 
Component Elements Properties Metric English Comments
Aluminum, Al 4.00 - 6.00 % 4.00 - 6.00 %
Carbon, C <= 0.100 % <= 0.100 %
Hydrogen, H <= 0.0150 % <= 0.0150 %
Iron, Fe <= 0.500 % <= 0.500 %
Nitrogen, N <= 0.0300 % <= 0.0300 %
Other, each <= 0.0500 % <= 0.0500 %
Other, total <= 0.300 % <= 0.300 %
Oxygen, O <= 0.200 % <= 0.200 %
Tin, Sn 2.00 - 3.00 % 2.00 - 3.00 %
Titanium, Ti 89.855 - 94.0 % 89.855 - 94.0 % As Balance; Elemental Compostions per ASTM B265

 

Users viewing this material also viewed the following:
Titanium Ti-5Al-2.5Sn, ELI, Annealed
Titanium Ti-3Al-2.5V (Grade 9), alpha annealed
Titanium Ti-6Al-2Sn-4Zr-2Mo-0.1Si; Duplex Annealed
Titanium, Ti
Titanium Ti-6Al-4V (Grade 5), Annealed

MTA520 / 14127

 


--------------------------------------------------------------------------------

Machining performance

Download UNS R54520 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


--------------------------------------------------------------------------------

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


--------------------------------------------------------------------------------

Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


--------------------------------------------------------------------------------

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


--------------------------------------------------------------------------------

Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


--------------------------------------------------------------------------------

Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.


--------------------------------------------------------------------------------

 

Hot tags:UNS R54520 steel plate, UNS R54520 sheet, UNS R54520 square steel, UNS R54520 flat bar,UNS R54520 round bar,UNS R54520 forgings


Copyright © 1996-2011 Longhai Special Steel. All Rights Reserved.
Longhai steel is China's special steel inventory spot suppliers.  

The sender: ChenXueYang mobile: 13108107311; Machine: 0816-3653779, 0816-3646884; Fax: 0816-3639422; QQ: 2286637323, E-mail: chinasteelsuppliers. Com
Stainless Steel | Mould steel | Heat resistant steel | Tool steel | Bearing steel | Spring steel | Alloy steel | Nickel base alloy and high nickel containing steels | Cementation steels | Free-cutting steels | Cold extrusion steels | Nitriding steels | Chain steels | Carbon steel | Ti Alloy | High temperature high strength alloy and high-temperature alloy | Low alloy high-temperature steel |

 

 
 

 

Related hot word search:UNS R54520 round bar UNS R54520 Ti Alloy,forging UNS R54520 Ti Alloy,UNS R54520 Ti Alloy sheet,coil UNS R54520 Ti Alloy,UNS R54520 Ti Alloy flat bar,pipe UNS R54520 Ti Alloy,UNS R54520 Ti Alloy Lrregular

Prev:UNS R56400 Ti Alloy
Next:Grade1 Ti Alloy